Order-disorder phase transitions in Fe81Ga19-RE ALLOYS (RE = Dy, Er, Tb, Yb) according to neutron diffraction data

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

New data on the phase compositions and structural transformations in a number of Fe81Ga19 alloys doped with trace amount (≤ 0.2 at.%) of rare earth elements are presented. The data are obtained in neutron diffraction experiments performed with high resolution and in continuous temperature scanning mode when heated to 900 °C and subsequent cooling. It has been established that structural rearrangements proceed in a generally identical manner both in the original Fe81Ga19 alloy and in its doped analogues. Slow heating and subsequent cooling of the alloys (rate ±2 °C/min) leads to the formation of clusters of the D03 phase with sizes in the range (200–300) Å in the matrix of the disordered A2 phase. The sizes and volume fraction of clusters (~0.3 of the sample volume) weakly depend on the specific composition. The degree of ordering of the clusters atomic structure changes with temperature according to a second-order phase transition and is close to unity at room temperature. The search for structural ordering corresponding to the modified D03 phase, discovered in a number of electron diffraction studies, did not lead to a positive result.

Толық мәтін

Рұқсат жабық

Авторлар туралы

A. Balagurov

Joint Institute for Nuclear Research; National Research Technological University “MISiS”

Email: bekarys@jinr.ru
Ресей, Dubna, 141980; Moscow, 119049

B. Yerzhanov

Joint Institute for Nuclear Research

Хат алмасуға жауапты Автор.
Email: bekarys@jinr.ru
Ресей, Dubna, 141980

Б. Мухаметулы

Joint Institute for Nuclear Research; Al-Farabi Kazakh National University; Institute of Nuclear Physics of the Ministry of Energy of the Republic of Kazakhstan

Email: bekarys@jinr.ru
Ресей, Dubna, 141980; Almaty, 050040 Kazakhstan; Almaty, 050032 Kazakhstan

N. Samoylova

Joint Institute for Nuclear Research

Email: bekarys@jinr.ru
Ресей, Dubna, 141980

V. Palacheva

Joint Institute for Nuclear Research; National Research Technological University “MISiS”

Email: bekarys@jinr.ru
Ресей, Dubna, 141980; Moscow, 119049

S. Sumnikov

Joint Institute for Nuclear Research; National Research Technological University “MISiS”

Email: bekarys@jinr.ru
Ресей, Dubna, 141980; Moscow, 119049

I. Golovin

Joint Institute for Nuclear Research; National Research Technological University “MISiS”

Email: bekarys@jinr.ru
Ресей, Dubna, 141980; Moscow, 119049

Әдебиет тізімі

  1. Summers E.M., Lograsso T.A., Wun-Fogle M.J. Magnetostriction of binary and ternary Fe–Ga alloys // Mater. Sci. 2007. V. 42. P. 9582–9594.
  2. He Y., Jiang C., Wu W., Wang B., Duan H., Wang H., Zhang T., Wang J., Liu J., Zhang Z., Stamenov P., Coey J.M.D., Xu H. Giant heterogeneous magnetostriction in Fe–Ga alloys: Effect of trace element doping // Acta Mater. 2016. V. 109. P. 177–186.
  3. Emdadi A., Palacheva V.V., Balagurov А.M., Bobrikov I.A., Cheverikin V.V., Cifre J., Golovin I.S. Tb-dependent phase transitions in Fe-Ga functional alloys // Intermetallics. 2018. V. 93. P. 55–62.
  4. Jin T., Wang H., Golovin I.S., Jiang C. Microstructure investigation on magnetostrictive Fe100-xGax and (Fe100-xGax)99.8Tb0.2 alloys for 19 ≤ x ≤ 29 // Intermetallics. 2019. V. 115. P. 106628.
  5. Wu Y., Chen Y., Meng Ch., Wang H., Ke X., Wang J., Liu J., Zhang T., Yu R., Coey J.M. D., Jiang C., Xu H. Multiscale influence of trace Tb addition on the magnetostriction and ductility of <100> oriented directionally solidified Fe–Ga crystals // Ph

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. Neutron diffraction spectrum of Fe81Ga19Er0.2 alloy measured on HRFD (high resolution) at room temperature. The calculated peak positions (strokes) and Miller indices are given for cell D03.

Жүктеу (14KB)
Метадеректер
3. Fig. 2. Profiles of the diffraction peak 400 of Fe81Ga19 alloy(Dy, Tb)0.1, measured on HRFD (high resolution) before (curve 1, diamonds) and after (curve 2, crosses) slow heating. Curve 3 (triangles) is the profile of the peak 300 (d = 1.386 Å) of the standard polycrystal La11B6. The peaks are normalized in amplitude and aligned in interplane distance.

Жүктеу (17KB)
Метадеректер
4. Fig. 3. Williamson–Hall construction for the widths of the fundamental diffraction peaks of Fe81Ga19(Dy, Tb)0.1 alloy in the states before heating (rhombuses) and after cooling (triangles). Miller indices of peaks are indicated. The numbers indicate the values of the microstresses of these two states. The dashed line is a contribution from the diffractometer resolution function. The dot errors are close to the size of the characters.

Жүктеу (13KB)
Метадеректер
5. Fig. 4. Neutron diffraction spectra of Fe81Ga19 alloy(Dy, Tb)0.1, measured on HRFD (average resolution) at room temperature before slow heating to 900 °C (a) and after cooling (b) to CT. The positions of the peaks of phases D03 and A1 (on the spectrum after cooling) are indicated.

Жүктеу (29KB)
Метадеректер
6. Fig. 5. Williamson–Hall construction for widths of superstructural diffraction peaks of Fe81Ga19(Dy, Tb)0.1 alloy in the state after heating–cooling. The calm line is a contribution from the resolution function of the diffractometer. Point errors are statistical.

Жүктеу (11KB)
Метадеректер
7. Fig. 6. Diffraction spectra of Fe81Ga19Dy01 alloy measured during its reheating to 900 °C (+2 °C/min) and subsequent cooling to CT (-2 °C/min). The axis of temperature is from bottom to top, the axis of interplanar distances is from left to right. The initial state of the alloy is phase A2, upon cooling, clusters of the ordered phase D03 were formed in the matrix of phase A2 and A1 is present in a small amount. Miller indices of peaks belonging to phases A2 and D03 are given for cell D03. The measurement time of one spectrum is 1 min, in total the 2D map contains about 900 spectra.

Жүктеу (24KB)
Метадеректер
8. Fig. 7. Dependence on the temperature of the diffuse background averaged over the interval d = (2.6–2.8) Å, measured during heating and cooling of the Fe81Ga19Dy0 alloy.1. The change in the slope of the dependence correlates with the formation of clusters of the ordered phase D03.

Жүктеу (21KB)
Метадеректер
9. Fig. 8. Temperature dependences of the intensities of the main (400) and superstructural (311) diffraction peaks of the D03 phase of Fe81Ga19Er0.2 alloy at its two heats (up to 900 °C) and cooling. The dependencies for the 1st and 2nd heats and the 2nd cooling (1st, 2nd) are shown. The dependencies for the 1st cooling are not shown, as they are almost identical to the 2nd cooling. The intensity scales for the main and superstructural peaks are different.

Жүктеу (19KB)
Метадеректер
10. Fig. 9. Temperature dependences of the intensities of the main (220) and superstructural (311) diffraction peaks of Fe81Ga19Dy0.1 alloy during its first (a) and second (b) heating and cooling. The intensity scales for the main and superstructural peaks are different.

Жүктеу (26KB)
Метадеректер
11. Fig. 10. Dependence on the temperature of the unit cell parameter (right scale) of Fe81Ga19 alloy during its heating and subsequent cooling and the intensities of the main (220) and superstructural (311) peaks (left scale) during cooling (transition A2 → A2 + D03). Inclined lines are a description of experimental points by a linear function in a certain temperature range. The figures indicate the temperature coefficient of linear expansion (in units of 10-5 1/K).

Жүктеу (29KB)
Метадеректер
12. Fig. 11. Temperature dependence of the intensity of the superstructural (311) peak (left scale) and its width (right scale) of the Fe81Ga19Er0.2 alloy during its second heating (a) and subsequent cooling (b). The variations indicated at the points are statistical. The lines are shown for clarity.

Жүктеу (49KB)
Метадеректер
13. Figure 12. Neutron diffraction spectrum of Fe81Ga19(Dy, Tb)0.1 alloy, measured in the region of large dhkl after cooling of the alloy. The scale along the ordinate axis has been increased. The main and superstructural peaks of phase D03 (111, 200, 220, 311) and peaks of phase A1 (111, 200) are present. There are no peaks of the m-D03 (110, 211) phase in the marked dhkl intervals.

Жүктеу (15KB)
Метадеректер